Potentiodynamic and galvanostatic testing of NaFe0.95V0.05PO4/C composite in aqueous NaNO3 solution, and the properties of aqueous Na1.2V3O8/NaNO3/NaFe0.95V0.05PO4/C battery
By Vujkovi?, Milica; Mentus, Slavko
Published in Journal of Power Sources
NULL
2016
Abstract
Abstract The NaFe0.95V0.05PO4/C composite is synthesized by electrochemical ion displacement from LiFe0.95V0.05PO4/C composite in aqueous NaNO3 solution. A coulombic capacity amounting to ?105 and ?82 mAh g?1 at sodiation/desodiation rate of 500 and 5000 mAg?1, respectively, is evidenced. For the sake of comparison the same investigations is performed with LiFe0.95V0.05PO4/C composite in LiNO3 solution, and better capacity retention and rate performance is evidenced for NaFe0.95V0.05PO4/C one. This advancement is found to be due a higher participation of pseudocapacity in the sodiation/desodiation charge storage process. An aqueous battery composed of NaFe0.95V0.05PO4/C cathode, belt-like Na1.2V3O8 anode and NaNO3 solution as an electrolyte, tested galvanostatically, displays long-life performance with only 10% of capacity fade after 1000 charge/discharge cycles.
Microsoft is Ending Support for Windows 7
Microsoft will discontinue support for Windows 7 on January 14, 2020 which means Gamry will also be discontinuing support for Windows 7. If you are upgrading to Windows 10, like many companies and institutions, you need to be running Version 7 of our s oftware . Please note that only USB and Ethernet-based instruments can run in Version 7. Eligible users can download the latest version of our software through our online Client Portal .
If you haven't already registered your instrument, you can do so through the Client Portal .
Please email Technical Support if you have any questions regarding this transition. Please be sure to include your instrument model and serial number when contacting us.