Comparison of the degradation behaviour of fusion-bonded epoxy powder coating systems under flowing and static immersion

By Wei, Y.H.; Zhang, L.X. & Ke, W.
Published in Corrosion Science NULL 2006

Abstract

The degradation of three different fusion-bonded epoxy (FBE) powder coating systems under flowing and static immersion condition has been monitored using electrochemical impedance spectroscopy (EIS) when exposed to 3% NaCl aqueous solution at 60 °C. The aim of this project was to determine the impact of flowing condition on the degradation of the protective properties of polymer coatings during exposure to corrosive medium. Using a rotating cylinder apparatus, the immersion tests under the flowing condition were performed. The relative permittivity of coating, ε r = C c δ ε 0 A, where the coating capacitance Cc was calculated from the high frequency data of impedance spectrum, was selected as the index to monitor property variation with immersion time. Experimental results showed that the flowing condition aggravated the deterioration of coatings. The results were interpreted in terms of a model in which flowing condition changes coating/solution interface state and then accelerates the ions to diffuse through the coating. The electrochemical results were in agreement with the final visual observation. The present investigation suggests that flowing test provides an effective accelerating way to evaluate the degradation of coating system.

Read Article » Back