Hydrothermal synthesis of Li4Ti5O12/C nanostructured composites: Morphology and electrochemical performance
By Vujković, Milica; Stojković, Ivana; Mitrić, Miodrag; Mentus, Slavko & Cvjetićanin, Nikola
Published in Materials Research Bulletin
NULL
2013
Abstract
Li4Ti5O12/C composites with low (3 wt.%) and high (33 wt.%) carbon black content as well as carbon-free Li4Ti5O12 were prepared in two steps under identical conditions: hydrothermal reaction at 130 °C and post-calcination at 400 °C. The X-ray diffraction experiments confirmed the spinel structure of Li4Ti5O12 in all samples. The carbon content altered significantly the morphology of obtained micro/nanoparticles. The Li4Ti5O12/C composite with the high carbon content showed the highest electrical conductivity (2.0 S cm-1), and displayed also extraordinary electrochemical performance: the cyclovoltammograms consisted of well defined reversible redox peaks at a scan rate as high as 10 mV s-1, while, by galvanostatic cycling, the coulombic capacity of 150 mAh g-1 was evidenced at a discharging rate of 10 C.
Microsoft is Ending Support for Windows 7
Microsoft will discontinue support for Windows 7 on January 14, 2020 which means Gamry will also be discontinuing support for Windows 7. If you are upgrading to Windows 10, like many companies and institutions, you need to be running Version 7 of our s oftware . Please note that only USB and Ethernet-based instruments can run in Version 7. Eligible users can download the latest version of our software through our online Client Portal .
If you haven't already registered your instrument, you can do so through the Client Portal .
Please email Technical Support if you have any questions regarding this transition. Please be sure to include your instrument model and serial number when contacting us.